*Solvent free, 100% solid content, safe, environmentally friendly and odor free.
*Rapid cure, can be sprayed forming on any bent, slope and vertical surfaces, no sagging.
*Coating film is compact, dense and flexibility, high adhesive strength with wood and foam substrate.
*Excellent impact resistance, collision resistance and abrasion resistance
*Excellent anticorrosion and chemical resistance to acids, alkali, salts etc.
*Good shock absorbing performance
*Excellent waterproof and moisture proof performance
*Excellent resistance to temperature variation
*Fast cure, application site back to service quickly
*Excellent durability to reduce maintenance cost of service life
*Extend the service life of sprayed structure
Wearable anticorrosion protection of coal chute, spiral separator, flotation tank, washing drum, transmission belt and other mining facilities.
|Appearance||Pale yellow liquid||Adjustable color|
|Solid content （%）||100||100|
|Mixing ratio（volume ratio）||1||1|
|Theoretical Coverage（dry film thickness）||1.03kg/㎡ film thickness:1mm|
|Hardness (Shore D)||ASTM D-2240||47|
|Elongation rate（%）||ASTM D-412||150|
|Tensile strength（Mpa）||ASTM D-412||20|
|Tear strength (N/km)||ASTM D-624||65|
|Wear resistance (750g/500r）/mg||HG/T 3831-2006||4.5|
|Adhesive strength（Mpa）concrete base||HG/T 3831-2006||3.1|
|Adhesive strength（Mpa) steel base||HG/T 3831-2006||11|
|Cathodic disbondment [1.5v,(65±5)℃，48h]||HG/T 3831-2006||≤15mm|
|Acid resistance 10%H2SO4 or 10%HCI,30d||No rust, no bubbles, no peel off|
|Alkali resistance 10% NaOH, 30d||No rust, no bubbles, no peel off|
|Salt resistance 30g/L,30d||No rust, no bubbles, no peel off|
|Salt spray resistance, 2000h||No rust, no bubbles, no peel off|
|Oil resistance 0# diesel, crude,30d||No rust, no bubbles, no peel off|
|(For reference: the above data is acquired based on GB / T9274-1988 test standard. Pay attention to the influence of ventilation, splash and spillage. Independent immersion testing is recommended if requires other specific data)|
|Product spray heating temperature||65℃-70°C|
|Pipe heating temperature||55℃-65℃|
|Recommend spray machine||GRACO H-XP3 Polyurea spray equipment|
|Spray gun||Air or machine self-cleaning coatings for spray gun|
|Recommend film thickness||1000-3000μm|
Agitate part B uniform prior to application, thoroughly mix the deposited pigments, or the product quality will be affected.
spray polyurea within the proper time if the substrate surface is primed. For the application method and interval time of SWD polyurea speical primer please refer to SWD companies’ other brochure.
Always apply SWD spray polyurea on a small area before large application to check the mix ratio, color and spray effect are correct. For detailed information of application please refer to the latest instruction sheet of the application instructions of SWD spray polyurea series.
|Substrate temperature||Dry||Foot traffic||Solid dry|
Note: the curing time varies with the environment condition especially the temperature and relative humidity.
*From the manufacturer date and on the original package sealed condition:
Packing: Part A 210kg/drum, part B 200kg/drum
Make sure the product package sealed well
* store in cool and ventilated place, avoid direct sunshine exposure.
For information and advice on the safe handling, storage and disposal of chemical products, users shall refer to the most recent Material Safety Data Sheet containing physical, ecological, toxicological and other safety related data.
SWD guarantee all technical data stated in this sheet are based on laboratory tests. Actual testing methods may vary due to different circumstances. Therefore please test and verify its applicability. SWD does not take any other responsibilities except the product quality and reserve the right of any modifications on the listed data without prior notice.
According to your actual needs, choose the most reasonable overall design and planning procedures